BRINELL HARDNESS TEST

This test is used: (1) to determine hardness of metallic materials, 

                             (2) to check the quality of the product,

                             (3) for uniformity of samples of metals, and 

                             (4) for uniformity of results of heat treatment.

              In this test, a standard hardened steel ball is pressed into the surface of the specimen by a gradually applied load which is maintained on the specimen for definite time. The impression so obtained is measured by a microscope and the Brinell Hardness Number (B.H.N) is found out by following equation:

B.H.N = Applied load in KG/Area of impression or indentation of steel ball in m2

             = P/A

Brinell Hardness Tester: Brinell hardness tester is shown in below Fig.

The hardness test is carried out as follows:

• Place the test sample on the top of the test table and rise it with the elevating screw, till the test sample just touches the ball.
• Apply the desired load (about 30' diameter of the ball in mm) either mechanically or by oil pressure.
• The steel ball during this period moves to the position of the sample and makes an impression or indentation.
• Measure the indentation diameter at two places, either on the screen provided with the machine or by coinciding the two points of a reading microscope.
• Using above equation, one can calculate BHN after substituting the values of P, D, d.

Precautions:

(1) The Brinell test should be performed on smooth, flat specimen from which dirt and scale have been cleaned.

(2) Successive impressions made too close to one another tend to produce high readings because of workhardening.

(3) The test should not be made on the specimen so thin that the impression shows through the metal nor should impressions be made too close to the edge of a specimen.

Advantages:

• It is widely applied in the industry due to the rapidity and simplicity with which they may be performed.
• Due to the small size of the impression produced we can achieve high accuracy.
• Also Rockwell hardness number can be converted to Brinell number using special table or chart.
•  For both hard and soft material it can be used.

Disadvantages:

1. The test machine is very heavy.
2. The area of indentation is quite large that it affects the surface quality. This is why, some it is considered as a destructive test.
3. The thickness of the test sample also limits its use, e.g., thin sheets will bulge or be destroyed during the test.
4. For very hard materials, the test results are unreliable. The ball gets flattened on hard surfaces.
5. One faces difficulty in measuring the indentation diameter accurately.