MICRO-Constituents of iron & steel

MICRO-Constituents of Iron & Steel:

          We can observe the various constituents of Fe and Steel produced due to decomposition of austenite under a microscope. The following are the important micro-constituents of Iron and Steel:

     1. Ferrite

     2. Cementite

     3. Pearlite

     4. Bianite

     5. Martensite

     6. Austenite

     7. Troosite, and

     8. Sorbite

Ferrite

i. Ferrite:

          Iron which contains little or no carbon is called Ferrite. This is a soft and ductile phase and is known as alpha iron generally by metallurgists. Ferrite is the name given to pure iron crystals. Ferrite is present to some extent in a great range of steels, particularly those low in carbon content, and it is also present, in soft cast iron. Ferrite has the following mechanical properties: Its KCU = 2.5 MJ/m2 , and HB = 80-100. Below the critical temperature, the slow cooling of low carbon steel produces ferrite structure. Ferrite is very soft and highly magnetic and does not harden when cooled rapidly. It forms smaller crystals when cooled from a bright red heat at a rapid rate.

Cementite

ii. Cementite:

          This is essentially an iron carbide Fe3C (of almost constant composition). It is extremely hard in nature and brittle, being harder than ordinary hardened steel or glass. Cementite increases with the proportion of carbon present, and the hardness and also the brittleness of cast iron is believed to be due to the presence of cementite in it.

          It contains 6.69% C and has a complex rhombic lattice. It is weakly ferromagnetic below 25°C, but loses this property on heating to 210°C. The melting temperature of cementite is difficult to determine, since cementite decomposes on heating. In experiments with laser-beam heating, its melting point has been measured to be 1260°C.